Inconel® 625 Plate

Inconel 625 is a nickel-chromium-molybdenum alloy with an addition of niobium that acts with the molybdenum to stiffen the alloy's matrix and thereby provide high strength without a strengthening heat treatment. Inconel 625 resists a wide range of severely corrosive environments and is especially resistant to pitting and crevice corrosion. Inconel 625 is used in chemical processing, aerospace and marine engineering, pollution-control equipment and nuclear reactors. Standard product forms aremore

Unit of Measure

Items	I625-1875 Inconel® 625 Plate	I625-250 Inconel® 625 Plate	I625-375 Inconel® 625 Plate	I625-500 Inconel® 625 Plate	I625-625 Inconel® 625 Plate
Material	N/A Inconel®
Shapeform	N/A Plates
Thickness	N/A 3/16 inches	N/A 1/4 inches	N/A 3/8 inches	N/A 1/2 inches	N/A 5/8 inches
Thickness	N/A 0.187 inches4.75 mm	N/A 0.25 inches6.3500 mm	N/A 0.375 inches9.52 mm	N/A 0.500 inches12.7 mm	N/A 0.625 inches15.87 mm
Plate Weight per Unit Area	N/A 0.06000 lbs/in²42.184176 kg/m²	N/A 0.08 lbs/in²56.245568 kg/m²	N/A 0.121 lbs/in²85.0714216 kg/m²	N/A 0.161 lbs/in²113.1942056 kg/m²	N/A 0.196 lbs/in²137.8016416 kg/m²
Alloy	N/A Inconel® 625
Basic Composition	N/A 1.0% Iron 16.3% Molybdenum 20.5% Chrominum 3.8% Tungsten 58.0% Nickel
Density	N/A 0.315 lbs/in³8.72 g/cm³
ASTM Specification	N/A ASME SB-443 ASTM B-443 SAE 5599 SAE 5869 UNS N06625
Melting Temperature Range	N/A 2350 to 2460 ºF1290 to 1350 ºC
Rupture Strength (1000 h at 1200°F/650°C)	N/A 52000 psi360 MPa
Rupture Strength (1000 h at 1400°F/760°C)	N/A 23000 psi160 MPa
Rupture Strength (1000 h at 1600°F/870°C)	N/A 7200 psi50 MPa
Rupture Strength (1000 h at 1800°F/980°C)	N/A 2600 psi18 MPa